How do you calculate corrosion rate of coupon?

Look up terms beginning with:

The weight loss of a corrosion coupon after exposure to a corrosive environment, expressed as mils (thousandths of an inch) per year penetration. Corrosion rate is calculated assuming uniform corrosion over the entire surface of the coupon. mpy = (weight loss in grams) * (22,300)/(Adt) mpy = corrosion rate ( mils per year penetration ) A = area of coupon (sq. in.) d = metal density of coupon (g/cm 3 ) t = time of exposure in corrosive environment (days). It is important to note that the calculated values using this formula are not representative in cases of severe pitting . Therefore, a complete report, including a visual inspection, is required to determine either the type of attack or the appropriate corrosion control program. Corrosion rate is also known as corrosion ratio.

Sign In to Access Premium Content

To download this file you first sign in to your Schlumberger account.

Don't have an account? Click below to get started.

Sign In Sign Up for an account

Corrosion Coupons Fundamentals

The most obvious method of assessing the corrosively of a cooling water system to a specific material is to expose a specimen or coupon made of that material for a given time in the flowing water. Coupons are made from specific alloys, which have been cleaned and pre-weighed with a known surface area. Coupons vary widely in size and shape. Some commonly used coupons are ½ inch (12.5 mm) wide, 3 inch (75 mm) in length, and 1/16 inch (1.6 mm) thick, having an approximately 3.4 in2 (2194 mm2) surface area. At selected time intervals, the coupons are removed, cleaned, and reweighed to determine the metal loss.

The weight loss is converted to overall thickness loss or average corrosion rate expressed in mpy, as follows:

Mpy = 22.25 x Δ W/(A x d x D)

Where

ΔW = weight change (mg), A = coupon surface area (in2).

D = metal density (g/cm3), and D = exposure time (days).

How to calculate the corrosion coupon exposed area (Ref. NACE RP0775)

 

Conversion to metric units, millimeter per year (mm/y), requires the above equation to be multiplied by 0.0254.

Mm/y = 0.0254 x mpy

Corrosion coupons are highly susceptible to initial corrosion because the metal surface is in an “active” state due to surface preparation. Coupons should not be touched during monitoring and installation process. Use of plastic gloves when handling the coupons is highly recommended. Normally, 30 days is a typical test period for low-corrosivity water under 10 mpy (0.25 mm/y). Low-corrosivity water usually contains chemical treatments to stifle corrosion attack. Exposure periods less than 30 days can yield misleading results. Frequently, long-term tests are required for up to 90 days’ exposure. During this time frame three sets of coupons are normally placed in a test rack and changed in a sequence of 30-, 60-, and 90- day intervals. Normally, the longer the exposure period, the lower the measured average corrosion rate and the more closely the coupons will approximate conditions in the system. Figure 1 graphically shows the decrease in corrosion rate with exposure time. Steady state is normally achieved in the 60- to 90-day time frame.

 

 

Screws and nuts made of nylon or plastic should be used to hold the coupons to the coupon holder. Mixed metallurgy should be avoided. Copper-base screws and nuts should not be used to hold carbon steel or stainless steel coupons. Galvanized screws and nuts should never be used.

Coupons having large amounts of deposits or tuberculation may indicate insufficient chemical treatment, unstable water characteristics, or highly corrosive conditions. Alternatively, deposits may have been transported from elsewhere in the system. Heavy, uniform deposits will reduce corrosion rates, since they can act as a protective barrier.

Visit www.yamathosupply.com

How do you calculate corrosion rate of coupon?

Corrosion Coupons Fundamentals